TY - JOUR
T1 - CALPHAD-Type Reassessment of Cu-Si and Full Assessment of the Al-Cu-Si Systems
AU - Kroupa, Ales
AU - Zobac, Ondrej
AU - Zemanova, Adela
AU - Richter, Klaus W.
N1 - Publisher Copyright:
© The Author(s) 2024.
Accession Number
WOS:001367956600001
PY - 2024/12
Y1 - 2024/12
N2 - The theoretical assessment of the Al-Cu-Si was carried out in this work based on recent experimental studies (Riani et al. in Intermetallics, 17:154-164, 2009; He et al. in CALPHAD, 33:200-210, 2009. http://dx.doi.org/10.1016/j.calphad.2008.07.015; Ponweiser N and Richter KW in J. of Alloys and Compd, 512:252-263, 2012; Hallstedt et al. in CALPHAD, 53:25-38, 2016; Zobac et al in J Mater Sci, 55:5322-15333, 2020). The reassessment of the Cu-Si system was also carried out in the scope of this work, as experimental data indicates reasonable solubility of Al in all intermetallic phases in the Cu-Si binary system, and the stoichiometric models used in previous assessments of the Cu-Si binary system are not fully suitable for the extension into the ternary system. Excellent agreement was reached for the reassessment of the Cu-Si system with previous works, and new original results were obtained during the assessment of the ternary system. The high solubility of Si in the β(bcc) phase at high temperatures was modelled to explain experimental inconsistencies in the Cu-rich corner between 600 and 800 °C, and this assumption was confirmed experimentally. All main features of the experimental Al-Cu-Si phase diagram were reproduced well by theoretical modelling.
AB - The theoretical assessment of the Al-Cu-Si was carried out in this work based on recent experimental studies (Riani et al. in Intermetallics, 17:154-164, 2009; He et al. in CALPHAD, 33:200-210, 2009. http://dx.doi.org/10.1016/j.calphad.2008.07.015; Ponweiser N and Richter KW in J. of Alloys and Compd, 512:252-263, 2012; Hallstedt et al. in CALPHAD, 53:25-38, 2016; Zobac et al in J Mater Sci, 55:5322-15333, 2020). The reassessment of the Cu-Si system was also carried out in the scope of this work, as experimental data indicates reasonable solubility of Al in all intermetallic phases in the Cu-Si binary system, and the stoichiometric models used in previous assessments of the Cu-Si binary system are not fully suitable for the extension into the ternary system. Excellent agreement was reached for the reassessment of the Cu-Si system with previous works, and new original results were obtained during the assessment of the ternary system. The high solubility of Si in the β(bcc) phase at high temperatures was modelled to explain experimental inconsistencies in the Cu-rich corner between 600 and 800 °C, and this assumption was confirmed experimentally. All main features of the experimental Al-Cu-Si phase diagram were reproduced well by theoretical modelling.
KW - Al-Cu-Si phase diagram
KW - CALPHAD
KW - Critical reassessment
KW - Cu-Si
KW - γ_brass phase
UR - http://www.scopus.com/inward/record.url?scp=85211480615&partnerID=8YFLogxK
U2 - 10.1007/s11669-024-01160-5
DO - 10.1007/s11669-024-01160-5
M3 - Article
AN - SCOPUS:85211480615
SN - 1547-7037
VL - 45
SP - 1206
EP - 1243
JO - Journal of Phase Equilibria and Diffusion
JF - Journal of Phase Equilibria and Diffusion
IS - 6
M1 - 173107
ER -