TY - JOUR
T1 - Short-range order kinetics during post-deformation annealing in different
AU - Spanl, Markus
AU - Rosenkranz, Peter
AU - Püschl, Wolfgang
AU - Korner, Alfred
AU - Pfeiler, Wolfgang
N1 - Zeitschrift: Materials Science and Engineering A
DOI: 10.1016/S0921-5093(01)01282-5
Affiliations: Institut fük Materialphysik, University of Vienna, Strudlhofgasse 4, Vienna A-1090, Austria
Adressen: Pfeiler, W.; Institut fük Materialphysik; University of Vienna; Strudlhofgasse 4 Vienna A-1090, Austria; email: [email protected]
Import aus Scopus: 2-s2.0-0037083793
17.12.2007: Datenanforderung 2031 (Import Sachbearbeiter)
PY - 2002
Y1 - 2002
N2 - Alloys of Cu-15at.% Al, Ag-21at.% Zn and Au-14at.% Fe are compared with respect to short-range ordering in the recrystallized state and after high deformation by cold-rolling, respectively. Additional information on the defect annealing behaviour is gained from an investigation of microhardness and by microscopy. Π2002 Elsevier Science B.V. All rights reserved.
AB - Alloys of Cu-15at.% Al, Ag-21at.% Zn and Au-14at.% Fe are compared with respect to short-range ordering in the recrystallized state and after high deformation by cold-rolling, respectively. Additional information on the defect annealing behaviour is gained from an investigation of microhardness and by microscopy. Π2002 Elsevier Science B.V. All rights reserved.
U2 - 10.1016/S0921-5093(01)01282-5
DO - 10.1016/S0921-5093(01)01282-5
M3 - Article
SN - 0921-5093
VL - 324
SP - 54
EP - 57
JO - Materials Science and Engineering A: Structural Materials: Properties, Microstructures and Processing
JF - Materials Science and Engineering A: Structural Materials: Properties, Microstructures and Processing
IS - 1-2
ER -